Vitreous Silica Fiber Heating Cable Bearing 800 1000 Degree Celsius 0Cr20Ni80 Resistance Cable
Ni80Cr20 is a nickel-chromium alloy (NiCr alloy) characterized by high resistivity, good oxidation resistance and very good form stability. It is suitable for use at temperatures up to 1200°C,and hold a superior service life compared to Iron chromium alumium alloys.
Typical applications for Ni80Cr20 are electric heating elements in home appliances,industrial furnaces and resistors(wirewound resistors,metal film resistors), flat irons, ironing machines, water heaters, plastic moulding dies, soldering irons, metal sheathed tubular elements and cartridge elements.
1. Product Detail
1) Normal Composition(%)
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max |
| 0.03 | 0.02 | 0.015 | 0.60 | 0.75-1.60 | 20.0~23.0 | Bal | Max 0.5 | Max1.0 | - |
2)Typical Mechanical Properties(1.0mm)
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 420 | 810 | 30 |
3)Typical Physical Properties
| Density (g/cm3) | 8.40 |
| Electrical resistivity at 20℃(Ωmm2/m) | 1.09 |
| Conductivity coefficient at 20℃ (WmK) | 15 |
| 4)Coefficient of thermal expansion |
| Temperature | Coefficient of Thermal Expansion x10-6/℃ |
| 20 ℃- 1000℃ | 18 |
| 5)Specific heat capacity |
| Temperature | 20℃ |
| J/gK | 0.46 |
| Melting point (℃) | 1400 |
| Max continuous operating temperature in air (℃) | 1200 |
| Magnetic properties | non-magnetic |
Insulation Material Inspection: Vitreous Silica Material Batch No.: V19D01
| SiO2 | Infiltrant content | Fiberglass Nominal Diameter | Max Working Temperature (long time) | Tex |
| 98% | 0.9% | 8μm | 800℃ | 160 |
Insulation Material Inspection: Silica Fiber Material Batch No.: V19H03
| SiO2 | Infiltrant content | Fiberglass Nominal Diameter | Max Working Temperature (long time) | Tex |
| 99.95% | 0.8% | 7.8μm | 1000℃ | 140
|